Lackowski WM, Vasilyeva YB, Crooks RM, Kerwin SC, Hulse DA.

J Am Vet Med Assoc. 2007 Aug 15;231(4):562. 

Objective: To determine the microchemical and surface composition of tibial plateau leveling osteotomy (TPLO) plates before and after explantation.

Sample Population: 7 TPLO plates surgically removed from host dogs 6 to 54 months after implantation; 2 raw unpolished-and-unpassivated 316L TPLO plates; and 2 heat-treated, polished-and passivated, and cleaned 316L TPLO plates.

Procedures: Samples were removed by use of standard techniques to ensure the plate surface was not damaged. Sample pieces were dissolved and analyzed by inductively coupled plasma-mass spectrometry (ICP-MS) to determine bulk elemental composition. Other sample pieces were investigated by use of scanning electron microscopy (SEM), energy dispersive spectroscopy (EDS), and x-ray photoelectron spectroscopy (XPS) for determination of sample morphology, near-surface elemental composition, and surface elemental composition, respectively. To investigate the possibility of corrosion in situ, some samples were chemically corroded and analyzed. Results-ICP-MS confirmed that elemental composition of samples was consistent with 316L stainless steel. The SEM and EDS analyses revealed trace amounts of polishing materials and a nonuniform carbonaceous biofilm on < 1% of the surface area of samples removed from the host dogs. The XPS analysis indicated an increase in the chromium-to-iron ratio on passivated surfaces, with no difference between passivated samples before implantation and after explantation.

Conclusions and Clinical relevance: Composition of the TPLO plates was consistent with 316L stainless steel. No chemical or topographic changes were detected in TPLO plates that had been implanted in dogs for up to 54 months. A small amount of biofilm was evident on the surface of 2 plates. (Am J Vet Res 2007;68:908-916).